Low temperature heat capacity study of Ba2TiSi2O8 and Sr2TiSi2O8 Shi, Q.; Park, T.J.; Schliesser, J.; Navrotsky, A.; Woodfield, B.F.; The Journal of Chemical Thermodynamics 2014, 72, 77-84
Data
P = 101.325 kPa
T (K) Cp (J mol-1 K-1)
1.94 0.00454
4.97 0.0882
5.52 0.128
6.12 0.187
6.79 0.275
7.52 0.404
8.36 0.597
9.27 0.871
10.28 1.26
11.41 1.79
12.65 2.48
2.16 0.00614
14.03 3.42
15.55 4.61
17.26 6.12
19.15 7.98
21.25 10.29
23.58 12.98
26.15 16.21
29.01 19.97
32.18 24.22
35.70 29.02
2.40 0.00838
39.61 34.42
43.95 40.41
48.76 46.48
54.10 53.48
60.02 60.69
66.60 68.58
73.90 76.99
82.01 86.29
91.02 96.16
101.01 105.66
2.65 0.0112
111.12 114.82
121.18 123.69
131.26 131.77
141.30 139.4
151.42 146.8
161.50 153.74
171.54 160.22
181.66 166.86
191.73 172.88
201.82 178.86
2.95 0.0157
211.90 184.39
221.98 189.47
232.06 194.35
242.14 198.79
252.17 203.72
262.24 207.6
272.38 211.23
282.45 215.07
292.43 218.89
302.51 222.0
3.28 0.022
3.65 0.031
4.03 0.0433
4.47 0.0611
29637; barium titanium silicate (Ba2Si2TiO8); 05929