The heat capacity and entropy of the lithium silicides Li17Si4 and Li16.42Si4 in the temperature range from (2 to 873) K Thomas, D.; Zeilinger, M.; Gruner, D.; Hüttl, R.; Seidel, J.; Wolter, A.U.; Fässler, T.F.; Mertens, F.; The Journal of Chemical Thermodynamics 2015, 85, 178-190
Data
P = 100 kPa, x = 0.804 mol mol-1
T (K) Cp (J mol-1 K-1)
284.87 22.41
324.51 23.85
740.89 32.64
750.81 32.68
750.81 32.92
760.73 33.14
760.73 33.47
770.64 33.77
770.64 34.02
780.56 34.41
780.56 34.69
790.48 34.65
324.52 23.8
790.48 35.21
800.39 35.13
800.39 35.58
810.30 35.47
810.30 36.02
820.22 36.24
820.22 36.35
830.13 38.35
830.13 38.57
840.04 41.23
334.42 24.09
840.04 41.78
849.95 45.22
849.95 47.32
859.87 51.54
859.87 53.53
869.79 60.18
869.79 65.17
334.42 24.14
334.43 24.12
344.33 24.3
344.33 24.38
344.35 24.37
354.24 24.56
354.24 24.6
294.79 22.86
354.26 24.57
364.16 24.81
364.16 24.83
364.17 24.69
374.07 24.83
374.07 24.87
374.07 24.94
383.99 25.05
383.99 25.05
393.90 25.16
304.67 23.11
393.90 25.27
403.81 25.3
403.81 25.35
413.73 25.46
413.73 25.49
423.64 25.57
423.64 25.65
433.56 25.68
433.56 25.75
443.48 25.83
304.67 23.16
443.48 25.95
453.39 25.96
453.39 26.21
463.31 26.1
463.31 26.34
473.22 26.29
473.22 26.62
483.13 26.48
483.13 26.77
493.04 26.73
304.70 23.05
493.04 26.89
502.95 26.84
502.95 27.04
512.86 27.0
512.86 27.24
522.77 27.23
522.77 27.49
532.68 27.46
532.68 27.67
542.58 27.67
314.59 23.41
542.58 27.88
552.50 27.8
552.50 28.0
562.41 27.97
562.41 28.24
572.33 28.21
572.33 28.37
582.24 28.41
582.24 28.65
592.15 28.65
314.59 23.55
592.15 28.85
602.06 28.86
602.06 29.05
611.97 29.02
611.97 29.19
621.88 29.19
621.88 29.48
631.80 29.46
631.80 29.65
641.71 29.67
314.61 23.42
641.71 29.92
651.63 29.86
651.63 30.21
661.54 30.1
661.54 30.48
671.45 30.27
671.45 30.68
681.36 30.52
681.36 30.84
691.29 30.56
324.51 23.8
691.29 31.08
701.21 31.04
701.21 31.36
711.13 31.38
711.13 31.59
721.05 31.75
721.05 32.03
730.97 32.1
730.97 32.36
740.89 32.38
43511; lithium + silicon; 05184:05804