Heat capacities of some sugar alcohols as phase change materials for thermal energy storage applications Jia, R.; Sun, K.; Li, R.; Zhang, Y.; Wang, W.; Yin, H.; Fang, D.; Shi, Q.; Tan, Z.; The Journal of Chemical Thermodynamics 2017, 115, 233-248
Data
P = 101.325 kPa
T (K) Cp (J mol-1 K-1)
1 0.00082714
10 1.0039
15 3.2425
20 6.5371
25 10.449
30 14.714
35 19.232
40 23.949
45 28.762
50 33.53
55 38.167
2 0.0063311
60 42.756
65 47.51
70 52.032
75 56.375
80 60.609
85 64.742
90 68.776
95 72.716
100 76.566
110 84.011
3 0.021638
120 91.15
130 98.026
140 104.68
150 111.17
160 117.52
170 123.79
180 130.0
190 136.19
200 142.38
210 148.6
4 0.052694
220 154.86
230 161.19
240 167.6
250 174.1
260 180.7
270 187.42
273.15 189.56
280 194.26
290 201.22
298.15 207.0
5 0.10649
300 208.32
6 0.19103
7 0.31525
8 0.48981
9 0.7186
5128; xylitol; 00390