Heat capacities of RCoO3(s) (R = La, Nd, Sm Eu, Gd, Tb, Dy and Ho) by differential scanning calorimetry Patil, A.; Parida, S.; Dash, S.; Venugopal, V.; Thermochimica Acta 2007, 465, 25-29
- Journal: Thermochimica Acta
- Sample Quantity(ies): Molar heat capacity at constant pressure
- Methodology: Large sample (1 g) DSC
- Phase(s): Crystal
- Substances:
Data
| T (K) | Cp (J mol-1 K-1) |
| 130 | 46.4 |
| 220 | 69.6 |
| 230 | 72.6 |
| 240 | 75.3 |
| 250 | 77.9 |
| 260 | 80.0 |
| 270 | 83.7 |
| 280 | 86.9 |
| 290 | 89.7 |
| 298.15 | 92.1 |
| 300 | 92.4 |
| 140 | 48.7 |
| 325 | 99.8 |
| 350 | 106.7 |
| 375 | 112.6 |
| 400 | 119.8 |
| 425 | 126.8 |
| 450 | 129.4 |
| 475 | 135.3 |
| 500 | 144.5 |
| 525 | 150.0 |
| 550 | 158.6 |
| 150 | 51.2 |
| 575 | 168.4 |
| 600 | 178.2 |
| 625 | 184.6 |
| 650 | 190.1 |
| 675 | 195.2 |
| 700 | 197.1 |
| 725 | 197.2 |
| 750 | 194.4 |
| 775 | 188.5 |
| 800 | 183.8 |
| 160 | 53.6 |
| 825 | 176.4 |
| 850 | 170.0 |
| 170 | 56.1 |
| 180 | 58.7 |
| 190 | 61.3 |
| 200 | 63.9 |
| 210 | 66.8 |
27622; cobalt gadolinium oxide; 05411