Enthalpies of mixing of liquid In-Sn and In-Sn-Zn alloys Rechchach, M.; Sabbar, A.; Flandorfer, H.; Ipser, H.; Thermochimica Acta 2010, 502, 66-72
Data
P = 101 kPa, T = 773.15 K
x (mol mol-1) x (mol mol-1) HmE (kJ mol-1)
0.1515 0.7080 0.992
0.2097 0.7013 0.616
0.2103 0.5945 1.426
0.2197 0.6871 0.656
0.2215 0.5730 1.504
0.2302 0.6721 0.694
0.2338 0.5493 1.586
0.2414 0.6563 0.717
0.2473 0.5233 1.666
0.2534 0.6391 0.749
0.2605 0.4978 1.752
0.1586 0.6942 1.061
0.2665 0.6204 0.8
0.2746 0.4707 1.85
0.2805 0.6005 0.848
0.2897 0.4415 1.949
0.2957 0.5789 0.903
0.3066 0.4089 2.057
0.3119 0.5557 0.979
0.3245 0.3745 2.167
0.3300 0.5300 1.039
0.3439 0.3371 2.275
0.1663 0.6793 1.117
0.3501 0.5014 1.125
0.3647 0.2971 2.399
0.3698 0.4734 1.175
0.3867 0.2546 2.522
0.3912 0.4428 1.263
0.4096 0.2105 2.636
0.4151 0.4088 1.361
0.4331 0.1651 2.779
0.4419 0.3706 1.474
0.4595 0.1143 2.923
0.1741 0.6644 1.175
0.4711 0.3290 1.636
0.4879 0.0594 3.042
0.5039 0.2824 1.734
0.5388 0.2326 1.871
0.5760 0.1797 2.018
0.6179 0.1199 2.202
0.6629 0.0559 2.346
0.1821 0.6489 1.24
0.1908 0.6321 1.291
0.1915 0.7273 0.557
0.2002 0.6142 1.352
0.2004 0.7146 0.586
27892; tin + zinc + indium; 01897:04492:05191