Calorimetric study of AlNd2: Heat capacity. Standard Gibbs energy of formation Morishita, M.; Yamamoto, H.; Kodera, M.; Ikeda, K.; Miura, S.; Yamada, Y.; Thermochimica Acta 2011, 526, 90-98
Data
P = 101.325 kPa
T (K) Cp (J mol-1 K-1)
2.151 0.8396
4.072 2.809
91.14 26.36
95.45 26.37
99.73 26.49
104.0 26.61
108.3 26.65
112.6 26.74
116.9 26.72
121.2 26.78
125.5 26.72
129.8 26.67
4.282 3.093
134.0 26.77
138.3 26.81
142.6 26.97
146.8 26.95
151.1 27.04
155.4 27.01
159.7 26.93
164.0 26.99
168.3 27.12
172.6 27.08
4.490 3.38
176.9 27.2
181.2 27.26
185.5 27.14
189.8 27.14
194.1 27.14
198.3 27.21
202.6 27.44
206.9 27.36
211.2 27.35
215.5 27.48
4.705 3.673
219.8 27.48
224.1 27.64
228.4 27.65
232.7 27.61
237.0 27.52
241.3 27.5
245.6 27.95
249.8 27.71
254.1 27.92
258.4 27.8
4.913 3.971
262.7 27.77
267.0 27.72
271.3 28.15
275.6 27.76
279.9 28.06
284.2 28.25
288.5 28.11
292.8 28.27
297.1 28.29
301.5 28.22
5.122 4.282
5.177 4.343
5.328 4.571
5.524 4.815
5.736 5.023
2.367 1.016
5.948 5.221
6.156 5.44
6.362 5.633
6.569 5.743
6.774 5.889
6.980 6.064
7.186 6.234
7.391 6.437
7.596 6.646
7.801 6.846
2.581 1.201
8.006 7.013
8.204 6.953
8.407 6.62
8.613 6.23
8.819 5.945
9.025 5.776
9.228 5.667
9.431 5.598
9.437 5.599
9.634 5.571
2.795 1.394
9.840 5.554
10.04 5.573
10.20 5.561
10.39 5.603
10.60 5.69
10.81 5.744
11.01 5.812
11.21 5.88
11.41 5.952
11.63 6.046
3.010 1.604
11.84 6.143
12.03 6.237
12.24 6.337
12.44 6.442
12.66 6.573
12.86 6.675
13.06 6.796
13.26 6.922
13.47 7.055
13.68 7.208
3.226 1.824
13.77 7.145
13.88 7.299
14.10 7.441
14.28 7.621
14.48 7.747
14.69 7.885
14.92 8.025
15.12 8.197
15.23 8.285
15.32 8.377
3.438 2.061
15.77 8.706
16.30 9.115
16.83 9.61
17.36 10.08
17.88 10.46
18.09 10.52
18.42 10.87
18.95 11.22
19.48 11.63
20.09 11.62
3.649 2.3
20.59 11.44
21.10 10.32
21.61 10.49
22.17 11.13
22.39 11.25
26.70 13.57
31.01 15.8
35.30 17.93
39.60 19.66
43.89 21.19
3.860 2.548
48.19 22.54
52.48 23.47
56.77 24.17
61.06 24.73
65.35 25.19
69.65 25.58
73.95 25.83
78.25 25.98
82.54 26.16
86.85 26.23
28100; neodymium; 05513